| POLITETRAFLUORETILENO
CON F. VIDRIO Y MoS2 |
PTFE
+
|
|
FV
+ MoS2
|
|
| PROPIEDADES
MECANICAS A 23ºC |
UNIDAD
|
ASTM
|
DIN
|
VALORES
|
| PORCENTAJE
EN PESO DE CARGA |
%
|
|
|
15FV
+ 5M
|
| PESO
ESPECIFICO |
Grs/cm3
|
D-792
|
53479
|
2.18
a 2.27
|
| RES.
TRACCION (DEF. 3% Y A ROTURA) |
Kg/cm²
|
D-638
|
53455
|
48
- 135
|
| RES.
A COMPRESION ( DEF. 1% y 5%) |
Kg/cm²
|
D-695
|
53454
|
69
- 153
|
| APLASTAMIENTO
A 140 Kg/cm² DURANTE 24 Hs. |
%
|
D-621
|
|
11.6
|
| ALARGAMIENTO
A LA ROTURA (MINIMA) |
%
|
D-638
|
53453
|
160
|
| RES.
AL CHOQUE SIN ENTALLA |
Kg.cm/cm²
|
D-256
|
53455
|
NO
ROMPE
|
| DUREZA |
Shore
D
|
D-2240
|
53505
|
55
a 60
|
| COEF.
DE ROCE ESTATICO S/ACERO |
|
D-1894
|
|
0.08
a 0.10
|
| COEF.
DE ROCE DINAMICO S/ACERO |
|
D-1894
|
|
0.15
a 0.27
|
| RES.
AL DESGASTE POR ROCE |
|
|
|
ALTA
|
| P
x V LIMITE PARA VEL. 3 Mts/Min |
Kg/cm²xm/min
|
|
|
2.35
|
| P
x V LIMITE PARA VEL. 30 Mts/Min |
Kg/cm²xm/min
|
|
|
300
|
| P
x V LIMITE PARA VEL. 120 Mts/Min |
Kg/cm²xm/min
|
|
|
340
|
| P
x V PARA DESG. 0.13 mm EN 1000 Hs. S/LUB. |
Kg/cm²xm/min
|
|
|
110
|
| VEL.
DE DESLIZAMIENTIO MAX. RECOMENDADA |
m/min
|
|
|
60
|
|
| PROPIEDADES
TERMICAS |
UNIDAD
|
ASTM
|
DIN
|
VALORES
|
| TEMP.
DE USO CONTINUO |
ºC
|
|
|
-
260 a 260
|
| COEF.
DE DILAT. LINEAL DE 23 A 100ºC |
Por
ºC
|
D-696
|
53328
|
0.00015
|
| COEF.
DE DILAT. LINEAL DE 23 A 150ºC |
Por
ºC
|
D-696
|
53328
|
0.000158
|
| COEF.
DE DILAT. LINEAL DE 23 A 260ºC |
Por
ºC
|
D-696
|
53328
|
0.00020
|
| COEF.
DE CONDUCCION TERMICA |
Kcal/m.h.ºC
|
C-177
|
52612
|
0.29
|
|
| PROPIEDADES
ELECTRICAS |
UNIDAD
|
ASTM
|
DIN
|
VALORES
|
| CONSTANTE
DIELECTRICA A 60 HZ |
|
D-150
|
53483
|
2.71
|
| CONSTANTE
DIELECTRICA A 1 MHZ |
|
D-150
|
53483
|
2.68
|
| ABSORCION
DE HUMEDAD AL AIRE |
%
|
D-570
|
53472
|
0.01
|
| RESISTENCIA
SUPERFICIAL |
Ohms
|
D-257
|
53482
|
>10
a la 14
|
| RESISTENCIA
VOLUMETRICA |
Ohms-cm
|
D-257
|
53482
|
10
a la 14
|
| RIGIDEZ
DIELECTRICA EN AIRE |
Kv/mm
|
D-149
|
|
27
|
|
|
PROPIEDADES
QUIMICAS Y OTRAS.
|
|
| RESISTENCIA
A HIDROCARBUROS |
EXCEL
|
| RESISTENCIA
A ACIDOS DEBILES A TEMP. AMBIENTE |
BUENO
|
| RESISTENCIA
A ALCALIS DEBILES A TEMP. AMBIENTE |
BUENO
|
| RESISTENCIA
A PROD. QUIMICOS DEFINIDOS |
CONSULTAR
|
| EFECTO
DE LOS RAYOS SOLARES |
NO
AFECTAN
|
| APROBADO
PARA CONTACTO CON ALIMENTOS |
SI
|
| COMPORTAMIENTO
A LA COMBUSTION |
NO
ARDE
|
| PROPAGACION
DE LLAMA |
NULA
|
|